Magnetization of ultrathin (Ga,Mn)As layers | R. Mathieu
; B. S. S{o}rensen
; J. Sadowski
; U. Södervall
; J. Kanski
; P. Svedlindh
; P. E. Lindelof
; D. Hrabovsky
; E. Vanelle
; | Date: |
21 Aug 2002 | Journal: | Phys. Rev. B 68, 184421 (2003). | Subject: | Materials Science | cond-mat.mtrl-sci | Abstract: | Kerr rotation and Superconducting QUantum Interference Device (SQUID) magnetometry measurements were performed on ultrathin (Ga$_{0.95}$Mn$_{0.05}$)As layers. The thinner layers (below 250 AA) exhibit magnetic properties different than those of thicker ones, associated with different microstructure, and some degree of inhomogeneity. The temperature dependence of the field-cooled-magnetization of the layers is recorded after successive low temperature annealings. While the Curie temperature of the thicker layer (250 AA) is nearly unchanged, the critical temperature of the thinner layers is enhanced by more than 23 K after two annealings. Secondary Ion Mass Spectrometry (SIMS) experiments on similar layers show that Mn is displaced upon annealing. The results are discussed considering a possible segregation of substitutional and interstitial Mn atoms at the surface of the (Ga,Mn)As layers. | Source: | arXiv, cond-mat/0208411 | Services: | Forum | Review | PDF | Favorites |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser claudebot
|
| |
|
|
|
| News, job offers and information for researchers and scientists:
| |