Synthesis and Physical Properties of Fese1/2te1/2 Superconductor | | V.P.S. Awana
; Anand Pal
; Arpita Vajpayee
; Monika Mudgel
; H. Kishan
; Mushahid Husain
; R. Zeng
; S.Yu
; Y. F. Guo
; Y.G. Shi
; K. Yamaura
; E. Takayama-Muromachi
; | | Date: |
5 Dec 2009 | | Abstract: | One of the most important properties of very recently reported FeSe based
superconductors is the robustness of their superconductivity under applied
magnetic field. The synthesis and control of superconductivity in FeSe based
compounds is rather a difficult task. Synthesis and physical property
characterization for optimized superconductivity of FeSe1/2Te1/2 at 13 K is
reported here. The compound crystallized in a tetragonal structure with lattice
parameters a = 3.8008(10) and c = 6.0187 (15) A. Magnetization measurements
indicated bulk superconductivity with lower critical field (Hc1) of around 180
Oe. By applying Ginzburg Landau (GL) theory, the Hc2(0) value is estimated to
be = 1840 kOe for the 90% of resistive transition. A heat capacity measurement
revealed bulk superconductivity by a hump at Tc near 13 K, and an anomalous
increase instead of expected decrease was observed under an applied magnetic
field. | | Source: | arXiv, 0912.0997 | | Services: | Forum | Review | PDF | Favorites | |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser claudebot
|
| |
|
|
|
|
News, job offers and information for researchers and scientists:
| |
REGISTER