MgB2 and Mg1-xAlxB2 single crystals: high-pressure growth and physical properties | J.Karpinski
; S.M.Kazakov
; J.Jun
; N.D.Zhigadlo
; M.Angst
; R.Puzniak
; A.Wisniewski
; | Date: |
29 Apr 2003 | Journal: | Physica C 408-410, 81 (2004) DOI: 10.1016/j.physc.2004.02.051 | Subject: | Superconductivity | cond-mat.supr-con | Abstract: | Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms. Typically they have transition temperatures between 38 and 38.6 K with a width of 0.3-0.5 K. Investigations of the P-T phase diagram prove that the MgB2 phase is stable at least up to 2190C at high hydrostatic pressure in the presence of Mg vapor under high pressure. Substitution of aluminum for magnesium in single crystals leads to stepwise decrease of Tc. This indicates a possible appearance of superstructures or phases with different Tc’s. The upper critical field decreases with Al doping. | Source: | arXiv, cond-mat/0304658 | Services: | Forum | Review | PDF | Favorites |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser claudebot
|
| |
|
|
|
| News, job offers and information for researchers and scientists:
| |