Through-thickness superconducting and normal-state transport properties revealed by thinning of thick film ex situ YBa2Cu3O7-x coated conductors | | D.M. Feldmann
; D.C. Larbalestier
; R. Feenstra
; A. A. Gapud
; J. D. Budai
; T.G. Holesinger
; P.N. Arendt
; | | Date: |
6 Oct 2003 | | Subject: | Superconductivity; Materials Science | cond-mat.supr-con cond-mat.mtrl-sci | | Abstract: | A rapid decrease in the critical current density (Jc) of YBa2Cu3O7-x (YBCO) films with increasing film thickness has been observed for multiple YBCO growth processes. While such behavior is predicted from 2D collective pinning models under certain assumptions, empirical observations of the thickness dependence of Jc are believed to be largely processing dependent at present. To investigate this behavior in ex situ YBCO films, 2.0 and 2.9 um thick YBCO films on ion beam assisted deposition (IBAD) - yttria stabilized zirconia (YSZ) substrates were thinned and repeatedly measured for rho(T) and Jc(H). The 2.9 um film exhibited a constant Jc(77K,SF) through thickness of ~1 MA/cm2 while the 2.0 um film exhibited an increase in Jc(77K,SF) as it was thinned. Neither film offered evidence of significant dead layers, suggesting that further increases in critical current can be obtained by growing thicker YBCO layers. | | Source: | arXiv, cond-mat/0310123 | | Services: | Forum | Review | PDF | Favorites | |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser Mozilla/5.0 AppleWebKit/537.36 (KHTML, like Gecko; compatible; ClaudeBot/1.0; +claudebot@anthropic.com)
|
| |
|
|
|
|
News, job offers and information for researchers and scientists:
| |
REGISTER