29 March 2024 |
|
| | | |
|
Article overview
| |
|
Systematic induction of superconductivity in Y1-xCaxBa2Cu3O6.3 system | V.P.S. Awana
; Anurag Gupta
; M.A. Ansari
; S.B. Samanta
; R.B. Saxena
; H. Kishan
; Devendra Buddhikot
; S.K. Malik
; V. Ganesan
; A.V. Narlikar
; | Date: |
9 Mar 2004 | Subject: | Superconductivity; Strongly Correlated Electrons | cond-mat.supr-con cond-mat.str-el | Affiliation: | NPL, New Delhi, India), Devendra Buddhikot and S.K. Malik (TIFR, Mumbai, India), and V. Ganesan and A.V. Narlikar (IUC, Indore, INDIA | Abstract: | Compounds of series YBa2Cu3O7-d (d = 0.7), being synthesized by solid-state synthesis route with x = 0.0, 0.10, 0.15 and 0.20, crystallize in single-phase form with tetragonal structure (space group P4/mmm). The c-lattice parameter increases with increasing x, indicating successful substitution of Y3+ by bigger Ca2+ ion. Resistance versus temperature (R vs. T) measurements show that pristine sample (x = 0.0) is semiconducting down to 5 K. Induction of superconductivity is seen with an increase in x. The x = 0.10 sample exhibit the onset of superconducting transition (Tconset) at around 42 K without attaining zero resistance superconducting transition temperature (TcR=0) state down to 5 K. For x = 0.15 and 0.20 samples TcR=0 is observed at 25 K and 35 K with Tconset of 52 K and 61 K respectively. Thermo-electric power (S) measurements in temperature range of 5 - 300 K, exhibited TcS=0 at around 25 K and 35 K respectively for x = 0.15 and 0.20 samples. Further a sign change in S from +ve to -ve is observed at low temperatures for x = 0.0 sample. Room temperature +ve S value decreases with increase in x, indicating enhanced number of mobile holes. The Magneto-transport measurements under applied magnet ic fields of 3 and 6 Tesla show the broadening of superconducting transition for x = 0.15, and 0.20 samples. For x = 0.10 sample the superconducting transition is suppressed in applied fields of 3 and 6 Tesla. Our results will help in constructing the complete phase diagram of Y1-xCaxBa2Cu3O7-d compounds with various x and d. | Source: | arXiv, cond-mat/0403230 | Services: | Forum | Review | PDF | Favorites |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser claudebot
|
| |
|
|
|
| News, job offers and information for researchers and scientists:
| |