Synthesis, crystal structure, microstructure, transport and magnetic properties of SmFeAsO and SmFeAs(O0.93F0.07) | A. Martinelli
; M. Ferretti
; P. Manfrinetti
; A. Palenzona
; M. Tropeano
; M. R. Cimberle
; C.Ferdeghini
; R.Valle
; M. Putti
; A.S.Siri
; | Date: |
13 Jun 2008 | Abstract: | SmFeAsO and the isostructural superconducting SmFeAs(O0.93F0.07) samples were
prepared. Characterization by means of Rietveld refinement of X-ray powder
diffraction data, scanning electron microscope observation, transmission
electron microscope analysis, resistivity and magnetization measurements were
carried out. Sintering treatment strongly improves the grain connectivity, but,
on the other hand, induces a competition between the thermodynamic stability of
the oxy-pnictide and Sm2O3, hence worsening the purity of the sample. In the
pristine sample both magnetization and resistivity measurements clearly
indicate that two different sources of magnetism are present: the former
related to Fe ordering at 140 K and the latter due to the Sm ions that orders
antiferromagnetically at low temperature. The feature at 140 K disappears in
the F-substituted sample and, at low temperatures a superconducting transition
appears. The magnetoresistivity curves of the F-substituted sample probably
indicates very high critical field values. | Source: | arXiv, 0806.2205 | Services: | Forum | Review | PDF | Favorites |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
browser Mozilla/5.0 AppleWebKit/537.36 (KHTML, like Gecko; compatible; ClaudeBot/1.0; +claudebot@anthropic.com)
|
| |
|
|
|
| News, job offers and information for researchers and scientists:
| |