MgB2 thick film with TC = 40.2 K deposited on sapphire substrate | Kaicheng Zhang
; Li-li Ding
; Cheng-gang Zhuang
; Li-ping Chen
; Chinping. Chen*
; Qing-rong Feng
; | Date: |
22 Jun 2006 | Subject: | Superconductivity | Abstract: | We have successfully deposited thick MgB2 film on the (0001) crystalline surface of sapphire by the method of hybrid physical-chemical vapor deposition (HPCVD). The film thickness is about 1.3 micron. It has a dense and interlaced structure. The film surface, shown by SEM, is stacked with MgB2 microcrystals. Transport measurements by the 4-probe technique have demonstrated that its critical temperature is about 40.2 K, with a sharp transition width of 0.15 K. The residual resistivity ratio (RRR) is about 11. By extrapolation, HC2(0) is determined as 13.7 T from the magneto-transport measurement. Also by hysteresis measurement and applying the Bean model, the critical current density is estimated as 5*1010 A/m2 in zero magnetic field. The present work has demonstrated that HPCVD is an effective technique to fabricate the MgB2 thick film with decent superconducting properties. Hence, it is important for the future superconducting application, in particular, as a crucial preliminary stage to fabricate superconducting tape. | Source: | arXiv, cond-mat/0606564 | Services: | Forum | Review | PDF | Favorites |
|
|
No review found.
Did you like this article?
Note: answers to reviews or questions about the article must be posted in the forum section.
Authors are not allowed to review their own article. They can use the forum section.
|
| |
|
|
|
| News, job offers and information for researchers and scientists:
| |